The addition of tin improves the corrosion resistance, especially in the sea water.
|
Chemical compound % |
Agent |
Cu |
Al |
Fe |
Mn |
Ni |
Pb |
Si |
Sn |
Zn |
Other |
Mass-volume g/cm3 |
Mini: |
59,0
|
-
|
-
|
-
|
-
|
-
|
-
|
0,5 |
Reste |
-
|
8,4 |
Maxi: |
61,0
|
-
|
0,1
|
-
|
0,2
|
0,2
|
-
|
1,0 |
- |
0,2
|
|
Mechanical properties of bars for die forging (EN 12165) : |
State |
Nominal size of the straight section |
Hardness |
Tensile strength
Rm
N/mm˛
approx. |
Conventional elastic limit at 0,2 %
Rp0,2
N/mm˛
approx. |
Stretching
A%
approx. |
Diameter
mm |
Size on flat mm |
from |
until and included |
from |
until and included |
HB
min. |
HV
min. |
M |
All sizes |
|
|
|
|
|
H080 |
6 |
80 |
6 |
60 |
80 |
85 |
(350) |
(160) |
(15) |
|
Mechanical properties of sections and rectangular bars (EN 12167): |
State |
Sizes |
Tensile strength Rm N/mm² min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching A % |
Hardness |
Section |
Rectangular bars thickness mm |
>
at |
<
or = |
HB
min. |
HV
min |
M
|
All |
All |
|
|
|
|
|
R460
|
-
|
-
|
6
|
460
|
(300)
|
(8)
|
-
|
-
|
H120 |
- |
- |
6 |
- |
- |
- |
120 |
125 |
R410 |
- |
6 |
60 |
410 |
(200) |
(10) |
- |
- |
H100 |
- |
6 |
60 |
- |
- |
- |
100 |
105 |
|