Non arsenical refined copper.
General engineering and building industry; processes that does not request a high conductivity. The oygen content will lead to a embrittlement if the metal is heated in a reducing atmosphere.
|
Chemical compound % |
Agent |
Cu |
Bi |
O |
P |
Pb |
Others |
Mass-volume g/cm3 |
total |
not included |
Mini: |
99,9
|
-
|
-
|
-
|
-
|
-
|
Ag,
Ni, O |
8,9
|
Maxi: |
-
|
-
|
0,100
|
-
|
-
|
0,05
|
|
|
Mechanical properties of plates, sheets and coils for general usings (EN1652): |
State |
Thickness |
Tensile strength Rm N/mm² |
Conventional elastic limit at 0,2Rp0,2 N/mm² . |
Stretching |
Hardness HV |
From |
to |
min. |
max. |
A50mm ep < or = 2,5 |
A ep > 2,5 |
min. |
max. |
R200
|
more than 5 |
200
|
250
|
(max.
100) |
-
|
42
|
-
|
-
|
H040
|
-
|
-
|
-
|
-
|
-
|
40
|
65
|
R220 |
0,2
|
5 |
220 |
260 |
(max
140) |
33 |
42 |
- |
- |
H040 |
0,2
|
5 |
- |
- |
- |
- |
- |
40 |
65 |
R240 |
0,2
|
15 |
240 |
300 |
(min.
180) |
8 |
15 |
- |
- |
H065 |
0,2
|
15 |
- |
- |
- |
- |
- |
65 |
95 |
R290 |
0,2
|
15 |
290 |
360 |
(min.
250) |
4 |
6 |
- |
- |
H090 |
0,2
|
15 |
- |
- |
- |
- |
- |
90 |
110 |
R360 |
0,2
|
2 |
360 |
- |
(min.
320) |
2 |
- |
- |
- |
H110 |
0,2
|
2 |
- |
- |
- |
- |
- |
110 |
- |
|
Mechanical properties of bars for general usings: (EN 12163) : |
State |
Implementation |
Diameter or size/flats mm |
Tensile strength Rm N/mm˛ min. |
Conventional elastic limit at 0,2Rp0,2 N/mm² |
Stretching |
Hardness |
from |
more than |
until |
A100mm
% min. |
A11,3
% min. |
A
% min. |
HB
min. |
HB
max. |
HV
min. |
HV
max. |
M
|
|
2
|
-
|
80
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
R2002
|
|
2
|
-
|
80
|
200
|
(80)
|
25
|
30
|
35
|
-
|
-
|
-
|
-
|
H0352 |
|
2 |
- |
80 |
- |
- |
- |
- |
- |
35 |
65 |
35 |
65 |
R250 |
|
2 |
- |
10 |
250 |
(220) |
8 |
10 |
12 |
- |
- |
- |
- |
R250 |
|
- |
10 |
30 |
250 |
(210) |
- |
- |
15 |
- |
- |
- |
- |
R230 |
|
- |
30 |
80 |
230 |
(190) |
- |
- |
18 |
- |
- |
- |
- |
H065 |
|
2 |
- |
80 |
- |
- |
- |
- |
- |
65 |
90 |
70 |
95 |
R300 |
|
2 |
- |
20 |
300 |
(280) |
5 |
6 |
8 |
- |
- |
- |
- |
R280 |
|
- |
20 |
40 |
280 |
(260) |
- |
- |
10 |
- |
- |
- |
- |
H085 |
|
2 |
- |
40 |
- |
- |
- |
- |
- |
85 |
110 |
90 |
115 |
R260 |
|
- |
40 |
80 |
260 |
(230) |
- |
- |
12 |
- |
- |
- |
- |
H075 |
|
- |
40 |
80 |
- |
- |
- |
- |
- |
75 |
100 |
80 |
105 |
R350 |
|
2 |
- |
10 |
350 |
(330) |
(3) |
(4) |
5 |
- |
- |
- |
- |
H100 |
|
2 |
- |
10 |
- |
- |
- |
- |
- |
100 |
- |
110 |
- |
2
Traited for solution treatment. |
|