| Chemical compound of rolled products (NFA 51-108) |
Agent: |
Sn |
Zn |
Pb |
P |
Cu |
Fe |
|
Mini
: |
3
|
-
|
- |
- |
Reste |
- |
- |
Maxi
: |
5
|
0,5
|
0,1 |
0,35 |
|
0,1 |
0,3 |
|
Mechanical characteristics of rolled products (NFA 51-108): |
States |
O |
H12 |
H14 |
H15 |
Rm
in N/mm˛ |
300
to 390 |
420
to 500 |
560
to 640 |
mini
700 |
| A%
min |
50 |
30 |
15 |
- |
| HV |
80 to
110 |
140
to 170 |
175
to 205 |
mini
200 |
|
Physical characteristics of rolled products (NFA 51-108): |
Conductivity
% IACS |
Conductivity
in Ohm.m |
Rp0,2
in N/mm˛ |
State
O |
State
H12 |
State
H14 |
State
H15 |
| 20
|
11,5.10-6 |
150 |
350 |
500 |
650 |
|
Chemical compound of wires (NFA 51-111): |
Agent: |
Sn |
P |
Cu |
Impurities |
Other agents
Total |
Fe |
Ni |
Pb |
Zn |
Mini
: |
3,0
|
0,1 |
Reste |
- |
- |
- |
- |
- |
Maxi
: |
5,5
|
0,4 |
|
0,1 |
0,3 |
0,05 |
0,3 |
0,3 |
|
Mechanical characteristics of wires (NFA 51-111): |
States |
Annealing |
Rm
in N/mm˛ |
295
to 390 |
| A%
min |
mini
45 |
|
Average physical and mechanical properties (for information only): |
| Average physical properties: |
Liquidus temperature (°C) |
Solidus temperature (°C) |
Solidification range (°C) |
Mass-volume at 20°C (kg/dm3) |
Linear expansion coefficient (10-6/°C) |
1070 |
950 |
120 |
8,80 |
18 |
Massive heat capacity at 20°C (J/kg.K) |
Heat conductivity at 20°C (W/m.K) |
Electrical conductivity at 20°C (%IACS) |
Electrical resistivity at 20° C (10-8 W.m) |
Coefficient
of resistivity temperature from 0 to
100°C (10-3°C) |
376 |
90 |
20 |
9 |
1 |
| Average
mechanical properties: |
Young's modulus (MPA) |
Modulus of twisting (MPA) |
Poisson's ratio |
122000 |
45000 |
±
0,35 |
|