Cu-a2 (Cu-FRHC)

 

Chemical compound (NFA 51-050)
Type
Cu mini en %
Max. electrical resistivity at 20 °C at annealing condition (C % IACS min)
Electrolytically refined, not deoxidized, with a guaranteed conductivity.

99,9

1,7241 µOhm.cm (100% IACS)

 

Mechanical characteristics of rolled products (NFA 51-100):
State

Rm en N/mm²

 A % mini

Hardness HV

O

mini 200

30

65

H11

from 230 to 280

20

from 55 to 80

H12

from 260 to 320

10

from 75 to 105

H14

mini 300

-

mini 100

 

Physical characteristics of rolled products (NFA 51-100):
Melting temperature (liquidus) in °C

Temperature of incipient meltng (solidus) in °C
 Mass volume in g/cm3
Electrical resistivity at   20 °C in µOhm.cm
 Conductivity in % IACS

Heat condictivity at 20°C in W/m.K

1083

1065

8,89 to 8,94

1,682 to 1,7241

100 to 102,5

400 to 412