CuAl6Ni2

 

Chemical compound of rolled products (NFA 51-113)
Agent
Cu
Al
Mn
Ni
Fe
Pb
Zn
Sn
Si
P
Misc.
Mini :

reste

5,5

-

1,7-

 -

-

 -

-

 -

-

 -

Maxi :

 -

 6,5

-

2,3

-

 0,02

-

 0,5

-

 -

0,5

 

Mechanical characteristics of rolled products (NFA 51-113):

State

Max. thickness in mm

Rm in N/mm² mini

Rp0,2 in N/mm² mini

A% mini

Annealing

30

345

140

30

Strain-aging

15

450

170

20

 

Physical characteristics of rolled products (NFA 51-113):

Mass volume in g/cm3

Coefficient of linear expansion from 20 to 200 °C in K-1.10-6

Mass heat capacity at 20°C in J/kg.K

Heat conductivity at 20°C in W/m.K

Electrical resistivity at 20°C (annealing) in µOhm.cm

Modulus of longitudinal elasticity in MPa

8,1

17

418

162,4

14

120000