AlZn6MgCu
No food using.
Aluminum alloy produced in limited quantity for some particular activity fields not covered by the European standard. No mechanical or physical characteristic is specified.
Shapes:
rolling plates, extrusion billets, extruded and drawn products, sheets, coils and thick plates. Forged parts.
Average mechanical characteristics - Properties:
Properties:
Corrosion
Anodizing
Strain, workability
Welding
Physical and elastic properties
Nominal chemical compound % (according to the standard EN 573-1):
Si
Fe
Cu
Mn
Mg
Cr
Ni
Zn
Remarks
Ti
Others
Al
Each
Total
0,12
0,15
1,5-2,0
0,10
2,1-2,6
0,05
0,05
5,7-6,7
0,10-0,16 Zr
0,06
0,05
0,15
Reste
Specific mechanical characteristics:
No standardized
(indicative values)
State
Rm
(MPa)
Rp0,2 (MPa)
A5
%
Hardness HV
T7
525
455
12
145
155
Top of the page
Properties
(for information only):
Corrosion :
General corrosion index
Not recommended
Corrosion in industrial atmosphere
Not recommended
Corrosion in sea atmosphere
Not recommended
Corrosion in country atmosphere
Satisfactory
Corrosion under stress
Good
Exfoliation index
Satisfactory
Intercrystalline corrosion
Satisfactory
Tapping index
Satisfactory
Top of the page
Anodizing:
Bright anodizing
Not recommended
Coloured anodizing
Not recommended
Hard anodizing
Satisfactory
Protecting anodizing
Good
Top of the page
Strain, workability:
T7
Cold working
Not recommended
Deep stamping
Strongly inadvisable
Strain by tension
-
Embossing ability
Strongly inadvisable
Extrusion ability
Satisfactory
Workability
Très
bon
Top of the page
Welding:
Welding by electron beam
Good
Gas welding
Not recommended
Arc welding
Not recommended
Spot welding
Good
Brazing
Not recommended
Soft brazing
Not recommended
Top of the page
Physical and elastic properties:
Elastic
Physical
E
G
n
T sol
T liq
C p
a
r
r el
l
EC
MPa
MPa
-
°C
°C
J kg-1 K-1
µm m-1 K-1
kg m-3
nW
m
W m-1 K-1
%IACS
72000
27100
0,33
475
630
857
23,7
2820
43
153
40
Legend:
E
Elastic modulus
MPa
G
Rigidity modulus
MPa
n
Poisson's ratio
T sol
Solidification temperature
°C
T liq
Melting temperature
°C
C p
Specific heating
J kg-1 K-1
a
Ratio of temperature expansion
µm m-1 K-1
r
Density
kg m-3
r el
Resistivity
nW m
l
Heat conductivity
W m-1 K-1
EC
Electrical conductivity
%IACS
Top of the page