AlSi1MgMn
(AGSM0,7)
Aluminum for food using. |
Mechanical characteristics :
Properties:
|
Nominal chemical compound % (according to the standard EN 573-1): |
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Ti
|
Others
|
Al
|
Each
|
Total
|
0,7-1,3
|
0,5
|
0,10
|
0,4-1,0
|
0,6-1,2
|
0,25
|
0,20
|
0,10
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Sheets
(according to the standard EN 485-2) : |
State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Bending radius |
Hardness HBS |
More than |
until |
mini |
maxi |
mini |
maxi |
A
50 |
A |
180° |
90° |
O |
>0,4
1,5
3,0
6,0
12,5 |
1,5
3,0
6,0
12,5
25,0 |
- |
150
150
150
150
155 |
- |
85
85
85
85
|
14
16
18
17
|
16 |
1,0
e
1,0
e
|
0,5
e
1,0
e
1,0
e
2,0
e
|
40
40
40
40
40 |
T4
T
451 |
>
0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
205
205
205
205 |
- |
110
110
110
110 |
- |
- |
12
14
15
14 |
3,0
e
3,0
e
|
1,0
e
1,5
e
3,0
e
4,0
e
|
58
58
58
58 |
T451 |
12,5
40,0 |
40,0
80,0 |
205
205 |
- |
110
110 |
- |
- |
13
12 |
- |
- |
58
58 |
T42 |
>0,4
1,5
3,0
6,0
12,5
40,0 |
1,5
3,0
6,0
12,5
40,0
80,0 |
|
- |
|
- |
12
14
15
14
|
13
142 |
-
|
1,5
e
2,0
e
3,0
e
4,0
e
|
57
57
57
57
57
57 |
T6
T651
T62 |
>
0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
310
310
310
310 |
- |
260
260
260
255 |
- |
- |
6
7
10
9 |
-
|
2,5
e
3,5
e
4,5
e
6,0
e |
94
94
94
91 |
|
12,5
60,0
100,0
150,0 |
60,0
100,0
150,0
175,0 |
|
- |
|
- |
- |
8
7
6
4 |
-
|
- |
89
89
84
43 |
|
Top of the page
Sheets in
relief
(according to the standard EN 1386): |
State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Bending radius min recommended at 90° |
More than |
until |
mini |
maxi |
Mini |
Maxi |
A
50 |
A |
O
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
-
-
-
-
|
150
150
150
150
|
-
-
-
-
|
85
85
85
85
|
6
8
10
12
|
-
-
-
12
|
2,0 t
2,0 t
2,0 t
-
|
T4
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
205
205
205
205
|
-
-
-
-
|
110
110
110
110
|
-
-
-
-
|
6
8
10
12
|
-
-
-
12
|
4,0 t
4,0 t
4,0 t
-
|
T6 |
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
310
310
310
310
|
-
-
-
-
|
260
260
260
260
|
-
-
-
-
|
2
3
4
6
|
-
-
-
6
|
-
-
-
-
|
T61
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
280
280
280
280
|
-
-
-
-
|
205
205
205
205
|
-
-
-
-
|
3
4
6
9
|
-
-
-
9
|
7,0 t
7,0 t
7,0 t
-
|
|
Top of the page
Extruded bars (according to the standard EN 755-2) : |
State |
Sizes
(mm) |
Rm
( MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
Diam |
Flat |
mini |
maxi |
mini |
maxi |
mini |
mini |
O/H111 |
<200 |
<200 |
- |
160 |
- |
110 |
14 |
12 |
T4 |
<200 |
<200 |
205 |
- |
110 |
- |
14 |
12 |
T6 |
<20
20
à 150
150
à 200
200
à 250
|
<20
20
à 150
150
à 200
200
à 250
|
|
- |
|
- |
|
|
|
Top of the page
Extruded tubes(according to the standard EN-755-2): |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
O/H111 |
£
25
|
-
|
160
|
-
|
110
|
14
|
12
|
T4
|
£
25
|
205
|
-
|
110
|
-
|
14
|
12
|
T6
|
£
5
5<e£25
|
290
310
|
-
-
|
250
260
|
-
-
|
8
10
|
6
8
|
|
Top of the page
Extruded sections (according to the standard EN-755-2) : |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
O/H111
|
Toutes
|
-
|
160
|
-
|
110
|
14
|
12
|
T4
|
£
25
|
205
|
-
|
110
|
-
|
14
|
12
|
Open section
T5
|
£
5 |
270
|
-
|
230
|
-
|
8 |
6 |
T6
|
£
5
5<e£25
|
290
310 |
-
-
|
250
260
|
-
-
|
8
10
|
6
8
|
Hollow section
T5
|
£
5
|
270
|
-
|
230
|
-
|
8
|
6
|
T6
|
£
5
5<e£10
|
290
310
|
-
-
|
250
260
|
-
-
|
8
10
|
6
8
|
|
Top of the page
Drawn bars
(according to the standard EN-754-2) : |
State |
Sizes
(mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
Diam |
Plat |
mini |
maxi |
mini |
maxi |
mini |
mini |
O/H111 |
<80 |
<80 |
- |
160 |
|
110 |
15 |
13 |
T4 |
<80 |
<80 |
205 |
- |
110 |
- |
14 |
12 |
T6 |
<80 |
<80 |
310 |
- |
255 |
- |
10 |
9 |
|
Top of the page
Drawn tubes
(according to the standard EN-754-2) : |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
O/H111 |
£
20
|
-
|
160
|
-
|
110
|
15
|
13
|
T4
|
£
20
|
205
|
-
|
110
|
-
|
14
|
12
|
T6
|
£
5
5<e£ 20
|
310
310
|
-
-
|
255
240
|
-
-
|
8
10
|
7
9
|
|
Top of the page
Wires according to the standard EN 1301-2: |
State |
Diameter
until and included |
Rm
(MPa) |
|
A100
m
% specific |
mini |
max |
H13
|
£
18
|
165
|
225
|
130
|
4
|
T39
|
³
6
|
310
|
-
|
-
|
-
|
T39
|
< 6
|
360
|
-
|
-
|
-
|
T4 |
£
20 |
205 |
- |
135 |
13 |
T6
|
£
20
|
300
|
-
|
270
|
10
|
T89
|
< 6
|
340
|
-
|
-
|
-
|
|
Top of the page
Properties
(for information only): |
Corrosion : |
General corrosion index |
Good
|
Corrosion in industrial atmosphere |
Good
|
Corrosion in sea atmosphere |
Good
|
Corrosion in country atmosphere |
Very good
|
Corrosion under stress |
Good
|
Exfoliation index |
Good
|
Intercrystalline corrosion |
Good
|
Tapping index |
Good
|
|
Top of the page
Anodizing: |
Bright anodizing |
Satisfactory
|
Coloured anodizing |
Good
|
Hard anodizing |
Good
|
Protecting anodizing |
Very good
|
|
Top of the page
Strain, workability: |
|
Recuit
|
T5
|
Cold working |
Good
|
Acceptable
|
Deep stamping |
Good
|
Acceptable
|
Strain by tension |
Good
|
Déconseillé
|
Embossing ability |
Good
|
Déconseillé
|
Extrusion ability |
Good
|
Good
|
Workability |
Déconseillé
|
Good
|
|
Top of the page
Welding: |
Welding by electron beam |
Good
|
Gas welding |
Good
|
Arc welding |
Very good
|
Spot welding |
Good
|
Brazing |
Good
|
Soft brazing |
Good
|
|
Top of the page
Physical and elastic properties: |
State |
Elastic |
Physical |
|
E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
O |
70000 |
26400 |
0.33 |
575 |
650 |
894 |
23.1 |
2710 |
31 |
216 |
55.5 |
T4 |
70000 |
26400 |
0.33 |
575 |
650 |
894 |
23.1 |
2710 |
41 |
167 |
42 |
T6 |
70000 |
26400 |
0.33 |
575 |
650 |
894 |
23.1 |
2710 |
39 |
172 |
44 |
|
Legend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
EC |
Electrical conductivity |
%IACS |
|
Top of the page |