AlMg1
Aluminum for food using. |
Mechanical characteristics::
Properties:
|
Nominal chemical compound % (according to the standard EN 573-1): |
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Others
|
Al
|
Each
|
Total
|
0,3
|
0,45
|
0,05
|
0,15
|
0,7-1,1
|
0,10
|
0,20
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Extruded bars (according to the standard EN 755-2) : |
State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
Diam
(D) |
Size on flat or thickness (S) |
mini |
max |
mini |
max |
F/H112 |
All |
All |
100 |
- |
40 |
- |
18 |
16 |
O/H111 |
All |
All |
100 |
150 |
40 |
- |
20 |
18 |
|
Top of the page
Extruded tubes (according to the standard EN-755-2) : |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
F/H112 |
All
|
100
|
-
|
40
|
-
|
18
|
16
|
O/H111
|
All
|
100
|
150
|
40
|
-
|
20
|
18
|
|
Top of the page
Extruded sections (according to the standard EN-755-2) : |
State |
Sizes
mm Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
F/H112 |
All
|
100
|
-
|
40
|
-
|
18
|
16
|
|
Top of the page
Drawn bars
(according to the standard EN-754-2) : |
State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
Diam |
Plat |
mini |
max |
mini |
max |
O/H111 |
< 80 |
<60 |
100
|
145 |
40
|
- |
18 |
16 |
H14 |
<40 |
<10 |
140 |
- |
110 |
- |
6 |
4 |
H18 |
<15 |
<2 |
185 |
- |
155 |
- |
4 |
2 |
|
Top of the page
Drawn tubes
(according to the standard EN-754-2) : |
State |
Sizes
mm Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
O/H111 |
£
20
|
100
|
145
|
40
|
-
|
18
|
16
|
H14
|
£
5
|
140
|
-
|
110
|
-
|
6
|
4
|
H18
|
£
3
|
185
|
-
|
155
|
-
|
4
|
2
|
|
Top of the page
Properties
(for information only): |
Corrosion: |
General corrosion index |
Very good
|
Corrosion in industrial atmosphere |
Very good
|
Corrosion in sea atmosphere |
Good
|
Corrosion in country atmosphere |
Very good
|
Corrosion under stress |
Very good
|
Exfoliation index |
Very good
|
Intercrystalline corrosion |
Very good
|
Tapping index |
Good
|
|
Top of the page
Anodizing: |
Bright anodizing |
Very good
|
Coloured anodizing |
Very good
|
Hard anodizing |
Very good
|
Protecting anodizing |
Very good
|
|
Top of the page
Strain,
workability: |
|
Annealing
|
Strain-aging
|
Cold working |
Very good
|
Correct
|
Deep stamping |
Very good
|
Correct
|
Strain by tension |
Very good
|
Satisfactory
|
Embossing ability |
Very good
|
Satisfactory
|
Extrusion ability |
Very good
|
Very good
|
Workability |
Not recommended
|
Satisfactory
|
|
Top of the page
Welding: |
Welding by electron beam |
Very good
|
Gas welding |
Good
|
Arc welding |
Very good
|
Spot welding |
Good
|
Brazing |
Satisfactory
|
Soft brazing |
Good
|
|
Top of the page
Physical and elastic properties: |
Elastic
|
Physical
|
E
|
G
|
n
|
Tsol
|
Tliq
|
Cp
|
a
|
r
|
rel
|
l
|
EC
|
MPa
|
MPa
|
-
|
°C
|
°C
|
J kg-1 K-1
|
µm m-1 K-1
|
kg m-3
|
nW m
|
W m-1 K-1
|
%IACS
|
69500
|
26100
|
0,33
|
630
|
655
|
899
|
23,5
|
2700
|
33
|
201
|
52
|
|
Légende : |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
EC |
Electrical conductivity |
%IACS |
Top of the page |