AlCu6BiPb
(AU5PbBi)
No food using.
Alloy of screw cutting with the 2030.
Excellent
workability due to the addition of lead. Mechanichal characteristics near the 2017.
Fields of using: unlimited needing an aluminum screw cut part.
International correspondences |
Mechanical characteristics:
Properties
:
|
Nominal chemical compound % (according to the standard EN 573-1) : |
Si
|
Fe
|
Cu
|
Zn
|
Remarks
|
Others
|
Al
|
Each
|
Total
|
0,4
|
0,7
|
5,0-6,0
|
0,3
|
0,2-0,6
Bi; 0,2-0,6 Pb
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Extruded bars (according to the standard EN 755-2): |
State |
Sizes
(mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A%
|
A50
% |
Diam |
Size/flat |
Mini |
Mini |
Mini |
Mini |
T4 |
<200 |
<60 |
275 |
125 |
14 |
12 |
T6 |
<75
75 ŕ 200 |
<60
- |
310
295 |
230
195 |
8
6 |
6 |
|
Top of the page
Extruded tubes (according to the standard EN-755-2): |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
T6 |
£
25
|
310
|
-
|
230
|
-
|
6
|
4
|
|
Top of the page
Drawn bars (according to the standard EN-754-2): |
State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
Diameter (D) |
Size on Flat or thickness (S) |
mini |
max |
mini |
max |
T3 |
£
40
40<D£ 50
50<D£ 80
|
£ 40
40<S£ 50
50<S£ 80
|
320
300
280
|
- -
-
|
270
250
210
|
- -
-
|
10 10
10
|
8 -
-
|
T8
|
£
80
|
£
80
|
370
|
-
|
270
|
-
|
8
|
6
|
|
Top of the page
Drawn tubes
(according to the standard EN-754-2): |
State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
mini |
max |
mini |
max |
T3 |
£
5 5<e£ 20
|
310 290
|
- -
|
260 240
|
- -
|
10 8
|
8 6
|
T8
|
£
20
|
370
|
-
|
275
|
-
|
8
|
6
|
|
Top of the page
Wires according the standard
EN 1301-2: |
State |
Diameter
until and included |
Rm
(MPa) |
Rp0,2
(MPa)
specific |
A100
m
% typique |
mini |
max |
T3 |
18 |
310 |
- |
295 |
6 |
T8 |
18 |
370 |
- |
310 |
4 |
|
Top of the page
Properties
(for information only): |
Corrosion : |
General corrosion index |
Not recommended |
Corrosion in industrial atmosphere |
Not recommended |
Corrosion in sea atmosphere |
Not recommended |
Corrosion in country atmosphere |
Satisfactory |
Corrosion under stress |
Not recommended |
Exfoliation index |
Satisfactory |
Intercrystalline corrosion |
Satisfactory |
Tapping index |
Not recommended |
|
Top of the page
Anodizing: |
Bright anodizing |
Not recommended |
Coloured anodizing |
Not recommended |
Hard anodizing |
Good |
Protecting anodizing |
Satisfactory |
|
Top of the page
Strain, workability: |
|
Strain aging
|
Cold working |
From not recommended to strongly inadvisable
|
Deep stamping |
Not recommended
|
Strain by tension |
Not recommended
|
Embossing ability |
Strongly inadvisable
|
Extrusion ability |
Good
|
Workability |
Excellent
|
|
Top of the page
Welding: |
Welding by electron beam |
- |
Gas welding |
Strongly inadvisable |
Arc welding |
Strongly inadvisable |
Spot welding |
Not recommended |
Brazing |
Not recommended |
Soft brazing |
Satisfactory |
|
Top of the page
Elastic and physical properties: |
State |
Elastic |
Physical |
|
E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
T3
/ T4 |
72500 |
27300 |
0.33 |
540 |
645 |
863 |
23 |
2840 |
44 |
152 |
39 |
T6
/ T8 |
72500 |
27300 |
0.33 |
540 |
645 |
863 |
23 |
2840 |
38 |
172 |
45.5 |
|
Légend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
EC |
Electrical conductivity |
%IACS |
Top of the page |
International correspondences: |
International
|
France
|
Germany
|
Great Britain
|
Italy
|
Switzerland
|
Spain
|
AA
|
NFA
|
Old
|
DIN
|
WNR
|
BS
|
Old
|
UNI
|
Old
|
SNCH
|
UNE
|
2011
|
2011
|
AU5PbBi
|
AlCuBiPb
|
3.1655
|
-
|
FC1
|
9002/5
|
6362
|
AlCu6BiPb
|
L
3192
|
Sweden
|
Russia
|
USA
|
Japan
|
Canada
|
Austria
|
Czechoslovakia
|
Finland
|
Norway
|
Holland
|
SS
|
GOST
|
ASTM
|
JIS
|
Old
|
CSA
|
|
CSN
|
SFS
|
NS
|
|
4355
|
-
|
2011
|
A2011
|
-
|
28S
/ CB60
|
A2011
|
-
|
-
|
-
|
14/11
|
|