AlMg1SiCu
(AGSUC)
Aluminum for food using. |
| High mechanical characteristics. Weldable, anodizable. Used in sheet metal working, tubing. |
| Mechanical characteristics:
Properties:
|
Nominal chemical compound % (according to the standard EN 573-1): |
|
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Ti
|
Others
|
Al
|
|
Each
|
Total
|
|
0,4-0,8
|
0,7
|
0,15-0,4
|
0,15
|
0,8-1,2
|
0,04-0,35
|
0,25
|
0,15
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Sheets
(according to the standard EN 485-2) : |
| State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Bending radius |
Hardness HBS |
| More than |
until |
mini |
maxi |
mini |
maxi |
A
50 |
A |
180° |
90° |
| O |
>0,4
1,5
3,0
6,0
12,5 |
1,5
3,0
6,0
12,5
25,0 |
- |
150
150
150
150
150 |
- |
85
85
85
85
85 |
14
16
19
16
|
16 |
1,0
e
1,0
e
|
0,5
e
1,0
e
1,0
e
2,0
e
|
40
40
40
40
40 |
| T4
T
451 |
>
0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
205
205
205
205 |
- |
110
110
110
110 |
- |
- |
12
14
16
18 |
1,5
e
2,0
e
|
1,0
e
1,5
e
3,0
e
4,0
e
|
58
58
58
58 |
| T451 |
12,5
40,0 |
40,0
80,0 |
205
205 |
- |
110
110 |
- |
- |
15.
14 |
- |
- |
58
58 |
| T42 |
>0,4
1,5
3,0
6,0
12,5
40,0 |
1,5
3,0
6,0
12,5
40,0
80,0 |
|
- |
|
- |
12
14
16
18
|
15
14 |
-
|
1,0
e
1,5
e
3,0
e
4,0
e
|
57
57
57
57
57
57 |
| T6
T651
T62 |
>
0,4
1,5
3,0
6,0 |
1,5
3,0
6,0
12,5 |
290
290
290
290 |
- |
240
240
240
240 |
- |
- |
6
7
10
9 |
-
|
2,5
e
3,5
e
4,0
e
5,0
e |
88
88
88
88 |
| |
12,5
40,0
80,0
100,0
150,0 |
40,0
80,0
100,0
150,0
175,0 |
|
- |
|
- |
- |
8
6
5
5
4 |
-
|
- |
88
88
88
84
81 |
|
hTop of the page
Sheets in
relief
(according to the standard EN 1386): |
| State |
Specified thickness (mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
Bending radius min recommended at 90° |
| More than |
until |
mini |
maxi |
Mini |
Maxi |
A
50 |
A |
|
O
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
-
-
-
-
|
150
150
150
150
|
-
-
-
-
|
85
85
85
85
|
6
8
10
12
|
-
-
-
13
|
2,0 t
2,0 t
2,0 t
-
|
|
T4
|
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
205
205
205
205
|
-
-
-
-
|
110
110
110
110
|
-
-
-
-
|
6
8
10
12
|
-
-
-
13
|
4,0 t
4,0 t
4,0 t
-
|
| T6 |
1,2
1,5
3,0
6,0
|
1,5
3,0
6,0
20,0
|
290
290
290
290
|
-
-
-
-
|
240
240
240
240
|
-
-
-
-
|
3
4
6
8
|
-
-
-
8
|
-
-
-
-
|
|
Top of the page
Extruded bars (according to the standard EN 755-2) : |
| State |
Sizes
(mm) |
Rm
( MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
| Diam |
Flat |
mini |
maxi |
mini |
maxi |
mini |
mini |
| O/H111 |
<200 |
<200 |
- |
150 |
|
110 |
16 |
14 |
T4 |
<200 |
<200 |
180 |
- |
110 |
- |
14 |
12 |
| T6 |
<200 |
<200 |
260 |
- |
240 |
- |
8 |
6 |
|
Topof the
page
Extruded tubes (according to the standard EN-755-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| O/H111 |
£
25
|
-
|
150
|
-
|
110
|
16
|
14
|
|
T4
|
£
25
|
180
|
-
|
110
|
-
|
15
|
13
|
|
T6
|
£
5
5<e£ 25
|
260
260
|
-
-
|
240
240
|
-
-
|
8
10
|
6
8
|
|
Top of the page
Extruded section (according to the standard EN 755-2) : |
State |
Sizes
|
Rm(
MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
mm |
mini |
mini |
mini |
mini |
T4 |
<25 |
180 |
110 |
15 |
13 |
T6 |
£5
5<e£ 25 |
260
260 |
240
240 |
9
10 |
7
8 |
|
Top of the
page
Drawn bars
(according to the standard EN-754-2): |
| State |
Sizes
(mm) |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% |
A50
% |
| Diam |
Flat |
mini |
maxi |
mini |
maxi |
mini |
mini |
| O/H111 |
<80 |
<80 |
- |
150 |
- |
110 |
16 |
14 |
T4 |
<80 |
<80 |
205 |
- |
110 |
- |
16 |
14 |
| T6 |
<80 |
<80 |
290 |
- |
240 |
- |
10 |
8 |
|
Top of the
page
Drawn tubes
(according to the standard EN-754-2): |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| O/H111 |
£
20
|
-
|
150
|
-
|
110
|
16
|
14
|
|
T4
|
£
20
|
205
|
-
|
110
|
-
|
16
|
14
|
|
T6
|
£
20
|
290
|
-
|
240
|
-
|
10
|
8
|
|
Top of the
page
Wires according to the standard EN 1301-2: |
| State |
Diameter
until and included |
Rm
(MPa) |
|
A100
m
% specific |
| mini |
max |
|
H13
|
£
18
|
150
|
210
|
120
|
4
|
|
T39
|
³
6
|
260
|
-
|
-
|
-
|
|
T39
|
< 6
|
310
|
-
|
-
|
-
|
| T4 |
£
20 |
205 |
- |
135 |
13 |
|
T6
|
£
20
|
290
|
-
|
260
|
10
|
|
T89
|
< 6
|
300
|
-
|
-
|
-
|
|
Top of the page
Properties
(for information only): |
Corrosion: |
| General corrosion index |
Bon
|
| Corrosion in industrial atmosphere |
Bon
|
| Corrosion in sea atmosphere |
Bon
|
| Corrosion under stress |
Très
bon
|
|
Top of the page
Anodizing: |
| Bright anodizing |
Acceptable
|
| Coloured anodizing |
Bon
|
| Hard anodizing |
Bon
|
| Protecting anodizing |
Très
bon
|
|
Top of the page
Strain, workability: |
| |
Recuit
|
T5
|
| Cold working |
Très
bon
|
Bon
|
| Deep stamping |
Très
bon
|
Acceptable
|
| Strain by tension |
Très
bon
|
Déconseillé
|
| Embossing ability |
Très
bon
|
Bon
|
| Extrusion ability |
Bon
|
Bon
|
| Workability |
Déconseillé
|
Acceptable
|
|
Top of the page
Welding: |
| Welding by electron beam |
Bon
|
| Gas welding |
Bon
|
| Arc welding |
Très
bon
|
| Spot welding |
Bon
|
| Brazing |
Bon
|
| Soft brazing |
Bon
|
|
Top of the page
Physical and elastic properties: |
| State |
Elastic |
Physical |
|
|
E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
| MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
| O |
70000 |
26300 |
0.33 |
580 |
650 |
895 |
23.3 |
2700 |
37 |
180 |
46.5 |
| T4 |
70000 |
26300 |
0.33 |
580 |
650 |
895 |
23.3 |
2700 |
43 |
155 |
40 |
T6 |
70000 |
26300 |
0.33 |
580 |
650 |
895 |
23.3 |
2700 |
40 |
166 |
43 |
|
| Legend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
| Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
| rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
| EC |
Electrical conductivity |
%IACS |
|
Top of the page |