AlSiMg
(AGS0,5)
Aluminum for food using. |
| Mechanical characteristics:
Properties:
|
Nominal chemical compound % (according to the standard EN 573-1): |
|
Si
|
Fe
|
Cu
|
Mn
|
Mg
|
Cr
|
Zn
|
Remarks
|
Ti
|
Others
|
Al
|
|
Each
|
Total
|
|
0,5-0,9
|
0,35
|
0,30
|
0,50
|
0,4-0,7
|
0,30
|
0,20
|
0,12-0,50 Mn+Cr
|
0,10
|
0,05
|
0,15
|
Reste
|
|
Specific mechanical characteristics: |
Extruded bars (according to the standard EN 755-2) : |
| State |
Sizes
mm |
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| Diam
(D) |
size on flat or thickness (S) |
mini |
max |
mini |
max |
| T6 |
£
25
25<D£ 50
50<D£ 100 |
£
25
25<D£ 50
50<D£ 100 |
270
270
270 |
-
-
-
|
225
225
215 |
-
-
-
|
10
8
8 |
8
-
-
|
|
Top of the page
Extruded tubes (according to the standard EN-755-2) : |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
|
T6
|
£
5
5<e£ 10
|
270
260
|
-
-
|
225
215
|
-
-
|
8
8
|
6
6
|
|
Top of the
page
Extruded sections (according to the standard EN-755-2): |
| State |
Sizes
mm
Thickness of wall
|
Rm
(MPa) |
Rp0,2
(MPa) |
A
% mini |
A50
% mini |
| mini |
max |
mini |
max |
| Open section
T4
|
£
25
|
180
|
-
|
90
|
-
|
15
|
13
|
|
T6
|
£
5
5<e£ 10
10<e£ 25
|
270
260
250
|
-
-
-
|
225
215
200
|
-
-
-
|
8
8
8
|
6
6
6
|
|
Hollow section
T4
|
£
10
|
180
|
-
|
90
|
-
|
15
|
13
|
|
T6
|
£
5
5<e£ 15
|
255
250
|
-
-
|
215
200
|
-
-
|
8
8
|
6
6
|
|
Top of the page
Properties
(for information only): |
Corrosion : |
| General corrosion index |
Good
|
| Corrosion in industrial atmosphere |
Good
|
| Corrosion in sea atmosphere |
Good
|
| Corrosion in country atmosphere |
Very good
|
| Corrosion under stress |
Good
|
| Exfoliation index |
Good
|
| Intercrystalline corrosion |
Good
|
| Tapping index |
Good
|
|
Top of the page
Anodizing: |
| Bright anodizing |
Satisfactory
|
| Coloured anodizing |
Good
|
| Hard anodizing |
Good
|
| Protecting anodizing |
Very good
|
|
Top of the page
Strain, workability: |
| |
T4
/ T6
|
| Cold working |
Satisfactory
|
| Deep stamping |
Satisfactory
|
| Strain by tension |
Not recommended
|
| Embossing ability |
Not recommended
|
| Extrusion ability |
Very good
|
| Workability |
Good
|
|
Top of the page
Welding: |
| Welding by electron beam |
Good
|
| Gas welding |
Good
|
| Arc welding |
Very good
|
| Spot welding |
Good
|
| Brazing |
Good
|
| Soft brazing |
Good
|
|
Top of the page
Physical and elastic properties: |
| Elastic |
Physical |
| E |
G |
n |
Tsol |
Tliq |
Cp |
a |
r |
rel |
l |
EC |
| MPa |
MPa |
- |
°C |
°C |
J kg-1 K-1 |
µm m-1 K-1 |
kg m-3 |
nW
m |
W m-1 K-1 |
%IACS |
69500 |
26200 |
0,33 |
605 |
655 |
892 |
23,3 |
2710 |
35 * |
193 * |
49,5 * |
|
| Legend: |
E |
Elastic modulus |
MPa |
G |
Rigidity modulus |
MPa |
n |
Poisson's ratio |
|
Tsol |
Solidification temperature |
°C |
Tliq |
Melting temperature |
°C |
| Cp |
Specific heating |
J kg-1 K-1 |
a |
Ratio of temperature expansion |
µm m-1 K-1 |
r |
Density |
kg m-3 |
| rel |
Resistivity |
nW m |
l |
Heat conductivity |
W m-1 K-1 |
| EC |
Electrical conductivity |
%IACS |
| * For state T6 |
|
Top of the page |